Friction Stir Welding of Steel: Part Three

概要:

The article describes mechanical properties, weld integrity and microstructure of a low carbon steel and a low carbon 12% chromium alloy steel. In general, mechanical testing and metallographic examinations showed good properties and reasonably uniform shaped double-sided weld profiles with no evidence of buried defects.

W.M. Thomas, P.L. Threadgill and E.D. Nickolas
TWI Ltd, Cambridge, United Kingdom

Weld Integrity of Low Carbon 12%Chromium Alloy Steel

Cross-weld tensile tests recorded an ultimate tensile stress of around 539 to 541 N/mm2 with failure occurring in the parent metal well away from the joint or the HAZ region as shown in Figure 1. Acceptable transverse face and root bends (bends with first pass in tension and bends with second pass in tension), typically achieved 180°, see Figure 2.

Figure 1: Cross-weld tensile test samples (3 off weld surfaces machined to uniform thickness before testing 3 off as welded)

Figure 2: Typical bend test results in 12 mm thick alloy steel plate, showing parent metal, and first pass and second pass in tension

Metallographic examination of selected sections, typically as shown in Figure 6 (see Friction Stir Welding of Steel: Part Two) shows a reasonably uniform shaped double-sided weld profile with no evidence of buried defects.

Average hardnesses were:

Parent metal   -  158HV10
HAZ             -  280HV10
TMAZ          -  230HV10

Weld Integrity of Low Carbon Steel

The cross-weld tensile tests gave an ultimate tensile stress of around 453 to 457 N/mm with failure occurring in the parent metal well away from the joint or HAZ region, broken tensiles are shown in Figure 3. Transverse 180° side bend tests are shown in figure 14.

Figure 3: Tensile test specimens of carbon steel FSW butt welds, showing failure in the parent metal away from the weld and HAZ

Figure 4: Three 180° side bends in low carbon steel FSW butt joints, plus one comparison parent metal bend

Metallographic examination of selected revealed a flow configuration (see Figure 7 within Friction Stir Welding of Steel-Part Two) not unlike those found on certain aluminium alloy welds. A reasonable shaped weld profile no evidence of buried defects, but some tool wear debris was observed.

Average hardnesses were:

Parent metal   -  131HV10
HAZ             -  149HV10
TMAZ          -  158HV10

Low carbon 12% Chromium Alloy steel

The weld region exhibited two distinct microstructural zones. One of these is the central weld thermomechanically affected (TMAZ) zone, which had transformed, with associated recrystallisation and grain growth. On both sides of the (TMAZ) central weld zone a HAZ region showed some transformation close to the weld but showed no evidence of grain growth. Further out, towards the parent material, the HAZ still showed a degree of tempering, but had not transformed. The HAZ zones on either side were similar in all features. Typical of this type of steel, the parent material showed a very fine ferritic/martensitic structure.

Within the TMAZ a range of ferrite and martensite structures had developed, a typical example is shown in Figure 5. Some light etching bands were present, towards the top of each weld pass. Energy dispersive x-ray micro analysis of these bands indicated the presence of some tool debris. Longitudinal weld sections, however, confirmed that no measurable reduction in weld depth had occurred after steady state welding conditions had been established. There was no evidence of buried defects within the weld region.

Figure 5: Microstructural bending in TMAZ weld region, showing banded two phase martensite and ferrit structure (12% chromium alloy steel weld)

Low Carbon Steel

The microstructure of the parent steel consisted of the expected ferrite.pearlite grains. The subcritical HAZ showed the expected spheroidization of pearlite, and the intercritical HAZ showed substantial grain refinement resulting from the partial transformation to austenite. The higher temperature supercritical HAZ in the centre of the weld had transformed to a bainitic/ferritic microstructure, with no evidence for martensite transformation.

The boundary between the HAZ, and the TMAZ (i.e. the point of which plastic deformation owing to the welding process first occurred) was difficult to identify, as no evidence of deformation without recrystalisation was observed. This suggests that the HAZ/TMAZ boundary occurred in the region heated above the AC3 temperature. This is in accordance with the peak temperature reached during friction stir welding of low carbon steel, which is probably around 1000-1100°C. A typical microstructure from the centre of the weld (in the TMAZ) is shown in Figure 6a, while Figure 6b shows the HAZ in the region of the AC3 isotherm, where areas of partial and complete transformation to austenite during the welding cycle are apparent.

Figure 6a: Banding between partially and completely transformed HAZ in friction stir welding in low carbon steel

Figure 6b: Microstructure of centre of friction stir weld in low carbon steel

Unlike the 12% chromium alloy steel, there was some evidence of tool debris within the weld region of the carbon steel examined, although examination of the tool after welding showed little wear. The debris existed as fine inclusions, exerting no apparent on the microstructure of the weld. It is needed.

The parent hardness of about 131 HV10 increases across the weld to a maximum of 160HV at the centre. These low values suggest the material was in the hot rolled condition before welding.

この記事は連載記事として掲載されております。詳細を見るには下記のリンクをクリックして下さい。

Total Materiaデータベースは世界の国々と広範な規格に関する数千種類の溶接に適した材料に関するデータを収録しております。

溶接に関する助言のほか必要に応じて、化学組成分、機械的特性、物理特性、炭素当量データなどの材料特性を御覧になれます。

高度な検索のページで材料グループのポップアップリストから’溶接フィラー材’を選び検索条件を決定します。さらに国/規格のフィールドを使い検索条件を絞ることもできます。

確定をクリックします。


選んだ材料の材料リストが表示されます。


結果リストで材料をクリックすると規格から導きだされるサブグループリストが表示されます。

そこから選んだ材料の特性を見る事ができさらにパワフルな相互参照表により類似材料、同等材料をみることもできます。


対象とする材料の特性データをクリックします。


Total Materiaデータベースをあなたにテスト評価を頂くために15万人以上の方が登録されている無料お試しコミュニティ-へ御招待致します。